冷轧退火对FeMnCoCrAl高熵合金组织和力学性能的影响

使用真空电弧炉熔炼出(Fe₅₀Mn₃₀Co₁₀Cr₁₀)₉₄Al₆合金,利用冷轧及在不同温度对合金进行退火,以期望得到由多尺度再结晶晶粒构成的层状结构;并对不同退火温度的样品进行拉伸性能测试。利用扫描电镜和EBSD对合金组织形貌进行表征,采用X射线衍射方法研究其相组成。结果表明:合金在铸态和冷轧后相组成未发生变化,700 ℃退火得到较好的多尺度再结晶晶粒的层状结构,其屈服强度为487 MPa,抗拉强度为708 MPa,断后伸长率为39%,表现出良好的综合力学性能。     

Effects of Rare Earths on Toughness of 31Mn2SiRE Wear-Resistance Cast Steel

The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.     

横泉水库大坝土料碾压试验

在取得土料场土料物理力学性质参数的情况下，遵循碾压试验基本原理、方法及参数组合，进行了现场碾压试验，通过试验成果的分析，得出了大坝碾压试验结论，为大坝土方填筑提供了技术依据。     

Effect of Strain Rate on Discontinuous Flow and Mechanical Characteristics of High-Nitrogenous Steel

Experimental study on the effect of strain rate on discontinuous flow and mechanical characteristics of the high-nitrogenous steel Kh23AG19F has been performed. Within the range of strain rates from 4.62 · 10^-5 to 1.85 · 10 ^-4 s^-1, discontinuous flow, reflected by serration on the tensile diagram, is chiefly determined by intergranular deformation mechanisms. Under strain rates over 1.85 · 10^-2 s^-1, combined deformation modes prevail, which cause a change in the character of discontinuous flow and transform a serrated tensile diagram into a wavy graph, with the yield stress of steel increased significantly.     

分层注水井智能测试调配技术试验评价

注水井智能测试调配技术在不改变原注水管柱的基础上，利用井下可调式堵塞器，通过地面电脑控制，实现了测试调配同步进行。通过7口井的现场试验及分析评价，表明该工艺具有测调精度高、测调时间短、测试资料准确等特点。     

双层悬空结构片状微电感研究

利用MEMS工艺制作了一种双层悬空结构的圆形片状微电感，并研究了其在S波段的性能。双层微电感的底层线圈制作在玻璃衬底平面上，外径为500μm，匝数为2，导线宽度70μm，导线间距15μm，顶层线圈的悬空高度为20μm，顶层线圈的匝数为1．5，其它结构参数与底层线圈相同。研究表明，所制作的双层结构微电感在2GHz～4GHz时其电感量达到2．2nH，其品质因数达到22。在制作过程中首次引入的光刻胶抛光工艺大大简化了微电感的制作过程。     

T-ZnO晶须增强环氧树脂复合材料的力学行为

研究了以四脚状氧化锌（T-ZnO）晶须为增强剂，环氧树脂复合材料的力学行为。结果表明，由具有三维空间结构的T-ZnO晶须为增强剂所制备的环氧树脂复合材料具有各向同性的力学性能，T-ZnO晶须填加质量分数为6%时，就可使材料的力学性能改善；拉伸强度提高到169%，拉伸功几乎提高了100%，冲击强度提高到300%，抗弯的断裂功提高到158%，而压缩强度略有下降。     

Mechanical properties of polyethylene mixtures crystallized under high pressure

The mechanical properties of a medium molecular weight polyethylene (MMW‐PE) and an ultrahigh molecular weight PE (UHMW‐PE) binary mixture with different weight fractions crystallized from the melt at 0.1 and 450 MPa were studied. The tensile modulus, yield stress, and strain were obtained as a function of the weight fractions in the PE mixtures at 25 and 85°C. The tensile modulus in the sample crystallized at 0.1 MPa decreased from 1.5 GPa of pure MMW‐PE to about 0.4 GPa of pure UHMW‐PE with the UHMW‐PE content but it did not decrease with the UHMW‐PE in the sample crystallized at 450 MPa in testing at 25°C. A decreasing rate of the storage modulus E′ of UHMW‐PE in a dynamic measurement for the sample crystallized at 0.1 MPa with the temperature is larger than that of the sample crystallized at 450 MPa. These experimental facts are interpreted in relation to the molecular motion and crystallinity of the sample. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1962–1968, 2003     

可控式机械密封设计

从机械密封的工作原理和失效分析入手,将自动控制技术引入机械密封,以改进机械密封的性能,使机械密封装置能够主动适应操作条件和工作环境的变化,提高其工作的可靠性和使用寿命,适用于要求较高的流体机械的轴端密封。     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。